Xiang Welding Industrial Co Ltd
Standard
Flux Cored Welding Wire Application
AWS E71T8-Ni1-J is applied in the situation where high ductility and element nickel are required. It especially fits in welding oil and gas pipelines coded from API X52 to X70
AWS E71T-1C is used for welding structures made of carbon steel and low-alloy structural steel with tensile strength higher than or equal to 490MPa. 
AWS E308LT1-1 is used for welding corrosion-resistant 06Cr19Ni10, 07Cr19Ni11Ti stainless steel structures and the working temperature should be below 300℃. It used for welding 301,302,304,301L, 308,308L and other stainless steel materials.
AWS E309LT1-1 can be used for welding petrochemical and other manufacturing equipment, chemical composition of the same type of stainless steel structure and composite steel, steel
AWS E316LT1-1 is used for welding ultra low carbon stainless steel such as 022Cr17Ni12Mo12, the stainless steel that cannot take the heat treatment after welding and welding Composite steel 
Flux Cored Arc Welding Wire (FCAW) , is used for welding structures made of carbon steel and low-alloy structural steel with tensile strength higher than or equal to 490MPa. Most widely used for welding some key structures like shipbuilding, mechanical manufacture, pressure vessels, boilers, petroleum machinery, chemical machinery, hoisting machinery etc.
Our advantages is stable arc, little spatter, less smoke; higher deposition efficiency; excellent welding performance; easy restrike.
Flux Cored Arc Welding Wire (FCAW)
Standard: AWS A5.20 E71T-1, E501t-1, AWS A5.20 E71T-GS
Sizes: 1.2mm, 1.4mm, 1.6mm
Packaging Details: OEM acceptable
Black and white plastic spools D100, D200, D270, D300
D100, 1KG/spool, 1000spools/pallet
D200, 5KG/spool, 200spools/pallet
D270, 15KG/spool, 72spools/pallet
D300, 15KG/spool, 72spools/pallet
Metal spools K300
K300, 15KG/spool, 72spools/pallet
Drum packing, 250KG/drum
Payment terms: 100% LC at sight or 30% TT in advance balance against copy of BL.
Trade terms: FOB, CFR, CIF, Loading Port: Xingang, Tianjin, China
Delivery Detail: Within 15 days after confirmation
Key words: welding wire, AWS A5.20 E71T-1, E501t-1, E71T-1, Flux Cored Arc Welding Wire , FCAW welding wire, flux cored welding wire, FCW wire,AWS A5.20 E71T-GS



Flux Cored Wire
Flux Cored Arc Welding Wire
FCAW welding wire production video
AWS E71T-GS is most popular for the home workshop welder because it works so well on 110 volt machines and can be used on such thin gauge steel. 
AWS A5.18 E70C-3M is a metallic flux cored wire designed to be used with Ar/CO2 for mild ssteel and 490N/mm2, high tensile steel, it's deposition rate is 10-30% higher than a solid wire. 
AWS A5.20 E70T-1C is a high deposition rate flux cored welding wire suitable for high speed fillet welding application in flat and horizontal position.
AWS A5.18 E70C-6M is a gas-shielded metal-cored wire that features smooth spray arc, low slag volume, low spatter, low diffusible hydrogen low fume emission and excellent low temperature impact toughness down to -400C.
AWS A5.20 E71T-1M is a flux-cored wire designed to be used with Ar/C02 gas. It's available for all-position welding with both single and multiple pass welds on mild and 490N/mm2 high tensile 
AWS A5.20 E71T-9CJ is a gas-shielded flux cored wire designed for mild steel and 490N/mm2 high tensile steel. It is suitable for all position welding.
AWS A5.20 E71T-5C is an all-position flux-cored wire designed to be used with C02 gas for 490N/mm2 grade high tensile steel.
AWS A5.20 E71T-1CJ 12CJ is a gas-shielded flux cored wire designed for mild steel and 490N/mm2 high tensile steel
AWS A5.20 E70T-4 is a self-shielded flux-cored wire, it is designed for on site general fabrication and structural work requiring
AWS A5.20 E70T-7 is a self-shielded flux cored wire designed for high penetration welding.
AWS A5.17 F7A6 EC1 Flux Cored Arc Welding Wire is a metal cored wire for submerged arc welding designed for welding 490N/mm2 grade high tensile steel and low temperature steel
AWS A5.26 EG72T 1 is a self-shielded flux-cored wire used for single pass, vertical up, electrogas welding of shipbuilding, heavy equipment fabrication and structural welding and storage tank.
AWS A5.26 EG82T-G is a self-shielded flux-cored wire used for single pass, vertical up, electrogas welding (EGW) of storage tank, shipbuilding, heavy equipment fabrication and structural welding.
AWS A5.29 E111T1-K3CJ offers excellent arc stability and low spatter with C02 shielding gas. It also has a fast freezing slag for all-position welding.
AWS A5.29 E81T1-A1C is a titania type flux cored arc welding wire, the weld metal contains about 0.5% molybdenum that help prevent deterioration in tensile strength after stress relief 
AWS A5.29 E81T1-B2C is a gas-shielded and all-position flux corded arc welding wire intended for 1-1.25%Cr-0.5%Mo low alloy steel welding.
AWS A5.29 E91T1-B3C is a gas-shielded and all-position flux-corded wire intended for 2.25%Cr-1%Mo low alloy steel welding.
AWS A5.29 E81T1-Ni1C is a titania type flux-cored arc welding wire for all-position MAG welding. It is designed for welding 590 N/mm2 high tensile steel used in low temperatures.
AWS A5.29 E81T1-Ni2C is a titania type flux-cored arc welding wire for all-position MAG welding. It provides good weldability with smooth bead appearance, less spatter and stable arc
AWS A5.29 E91T1-Ni2C is a titania type flux-cored wire for all-position welding. It provides good weldability with smooth bead appearance, less spatter and stable arc
AWS A5.29 E81T1-K2C a titania type flux-cored wire, is designed for welding 560 N/mm2 high tensile steel for low temperatures.
AWS A5.29 E81T1-Ni1MJ is a gas-shielded flux cored wire for all-position welding. It is designed for welding 590 N/mm2 high tensile steel for low temperatures
AWS A5.29 E81T1-W2C is a titania type flux-cored arc welding wire and suitable for butt or fillet MAG welding
AWS A5.22 E308HT1-1 Flux Cored Arc Welding Wire is special for 100% C02 gas and all-position welding.
AWS A5.22 E308LT0-1 Flux Cored Arc Welding Wire is designed for Flat position welding by gas shield of 100% CO2.
AWS A5.22 E308LT0-4 Flux Cored Arc Welding Wire is designed for Flat position welding by gas shield of mix gas (75- 80% Argon and 25—20% CO2).
AWS A5.22 E309LT1-1 Flux Cored Arc Welding Wire is designed for 100% CO2 gas shielding and all position welding.
AWS A5.22 E309LT0-1 Flux Cored Arc Welding Wire is designed for Flat position weiding by gas shield of mix gas (75—80% Argon and 25—20% Co2).
AWS A5.22 E309LT0-4 Flux Cored Arc Welding Wire is designed for flat position welding by gas shield of mix gas (75%-80%Argon and 25%-20%CO2).
AWS A5.22 E309LMoT1-1 Flux Cored Arc Welding Wire is a modified type of 309L with the addition of molybdenum.
AWS A5.22 E316LT1-1 Flux Cored Arc Welding Wire is designed for 100% CO2 gas shielding and all-position welding.
AWS A5.22 E316LT0-1 Flux Cored Arc Welding Wire is designed for flat position welding by gas shield of CO2 gas.
AWS A5.22 E316LT0-4 Flux Cored Arc Welding Wire is designed for flat position welding by gas shield of mix gas (75-80% Argon and 25—20% CO2 )
AWS A5.22 E317LT1-1 Flux Cored Arc Welding Wire is designed for 100% CO2 gas shielding and all-position welding wire.
AWS A5.22 E347T1-1 Flux Cored Arc Welding Wire is designed for 100% Co2 gas shielding and all-position welding wire.
AWS A5.22 E410NiMoT1-1 Flux Cored Arc Welding Wire is a gas-shielded flux-cored wire with better control of hydrogen levels and excellent impact toughness at 0℃.
AWS A5.22 E2209T1-1 is a flux cored arc welding wire that is suitable for the welding of duplex stainless steel such as UNS S31803 (Alloy 2205).
AWS A5.22 E2209T1-4 Flux Cored Arc Welding Wire is suitable to duplex stainless steel such as UNS S31803 (Alloy 2205).
AWS A5.34 ENiCrMo3T1-4 Flux Cored Arc Welding Wire is the rutile high nickel alloy flux cored wire.
AWS A5.20 E71T-1C Flux Cored Arc Welding Wire is a flux-cored wire designed to be used with C02 gas and it's all-position welding with both single and multiple pass welds on mild
Highly efficient E70T-1 wire that can increase productivity when welding in deep grooves compared to conventional wires with the same classification
RXR is an E70T-1 wire that has a higher level of de-oxidizing elements to handle mill scale, rust and other contaminants.
This wire has a basic slag system and is designed for use where deposit quality and properties are of a first concern. Weld metal hydrogens are very low making this wire more crack resistant than the acid slag types of wires.
This tubular wire combines excellent operator appeal with mechanical properties superior to most conventional E71T-1 wires. A soft quiet arc with virtually no spatter produces a weld deposit with diffusible hydrogen levels typically less than 5ml/100 g required by MIL-E-24403/1.
This wire has low smoke, spatter and excellent operator appeal For mild and some low alloy steels.
FabCO 73 has a very high amount of de-oxidizing elements to handle moderately mill scale, rust and other foreign contaminants
Designed as a low Manganese (Mn) E71T-1C product to assist with conformance to OSHA requirements and NIOSH and ACGIH recommendations for Manganese. This product offers reductions of Mn in the weld fume of 60-80% over a standard E71T-1C product with low diffusible hydrogen as well as enhanced operator appeal and excellent out of positional capability.
All position wire for both CO2 and mixed gas. For mild and low alloy steel applications.
The stiff arc action of this wire enhances the deep penetration for out of position welding. Designed for use welding carbon steels, or higher strength steels where the properties of an E71T-1 are deemed adequate.
Formulated to allow excellent impact values at lower temperatures. All position wire with low hydrogen levels.
All position wire for both CO2 and mixed gas. For mild and low alloy steel applications.
Formulated to allow excellent mechanical toughness properties at lower temperatures in both the as welded and post weld heat treat conditions. All position wire with low hydrogen levels.
AWS A5.20: E71T-1MJ H8, E71T-9MJ H8, E71T-12MJ H8,EN ISO 17632-A T42 4 P M21 2 H10 are Flux Cored Welding Wire ,.Formulated to allow excellent mechanical toughness properties at lower temperatures in both the as welded and post weld heat treat conditions. All position wire with low hydrogen levels.
AWS A5.29: E100T5-D2C Flux Cored Welding Wire can be used for the repair of manganese-moly castings, or components that must undergo post weld heat treatment and maintain a tensile strength in the neighborhood of 100,000 psi. The basic slag system ensures a low hydrogen weld deposit.
Intended for single and multiple pass applications in all positions. Designed for carbon and higher strength steels.
An all position tubular wire with higher impact values than most other E71T-1 wires. Single or multiple pass welds, easy slag removal and low spatter levels, allows this wire to be used in deep groove applications as well as standard joint configurations.
AWS A5.29: E101T1-GM Flux Cored Welding Wire minimizes the crack sensitivity in quench and tempered low alloy steels such as ASTM A514. Excellent impact properties at low temperatures.
AWS A5.29: E110T5-K4C H4 Flux Cored Welding Wire.Primarily used in the welding of T-1, A514, A517, HY-100, and similar quenched and tempered high strength and low alloy steels. The basic slag system produces a low hydrogen weld deposit reducing the chance of cracking.
AWS A5.29: E111T1-K3C Flux Cored Welding Wire.High strength all-postion gas-shieled flux core wire used to join quench and tempered steels like ASTM A514
Designed as a low Manganese (Mn) E71T-1M product to assist with conformance to OSHA requirements and NIOSH and ACGIH recommendations for Manganese. This product offers reductions of Mn in the weld fume of 60-80% over a standard E71T-1M product with low diffusible hydrogen as well as enhanced operator appeal and excellent out of positional capability.
Specially designed for use with high Argon shielding mixes such as 95%Ar/5% CO2.
AWS A5.29: E71T1-GM H8 Flux Cored Welding Wire.Designed as a low Manganese (Mn) E71T-1M product to assist with conformance to OSHA requirements and NIOSH and ACGIH recommendations for Manganese. 
Offers excellent properties on many higher strength steels.
This wire is used for welding high strength quench and tempered and low alloy steels like T-1, A514, A517, and Hy-100. The T-5 flux core uses a basic slag which keeps hydrogen content very low reducing the chance for cracking.
AWS A5.29: E81T1-K2CJ H8 is Flux Cored Welding Wire.All position wire designed for 100% CO2 gas. For mild and low alloy steel applications.
Designed as a low Manganese (Mn) replacement for E81T1-K2C products. Meets all requirements of E81T1-K2C classification except for the minimum Mn requirement.
This wire minimizes the crack sensitivity in quench and tempered low alloy steels such as ASTM A514.
AWS A5.29: E81T1-Ni1 MJ H4 is Flux Cored Welding Wire.Formulated to allow excellent mechanical toughness properties at lower temperatures in both the as welded and post weld heat treat conditions. All position wire with low hydrogen levels
AWS A5.29: E81T1-Ni2CJ H4, E81T1-Ni2MJ H4 Flux Cored Welding Wire .FabCO 803 is especially suited for those fine grained steels where low temperature CVN toughness is needed. Ideal for welding 2% Nickel steels. Provides a fast-freezing slag, low spatter, excellent arc characteristics, and high impact strengths at low temperatures.
For the welding of quenched and tempered low alloy grades of steels. Excellent impact values at low temperatures along with a low diffusible hydrogen content due to the basic slag system.
AWS A5.29: E91T1-B3C H4,E91T1-B3M H4 is Flux Cored Welding Wire.Suitable for use on materials having a similar composition, such as ASTM A387 or P21/P22 Pipe. Suitable for extended service at elevated temperature. Provides good puddle control and bead contour when welding in all positions. Provides versatility in procedure and application development.
Designed as a low Manganese (Mn) E71T-1C product to assist with conformance to OSHA requirements and NIOSH and ACGIH recommendations for Manganese. This product offers reductions of Mn in the weld fume of 60-80% over a standard E71T-1C product with low diffusible hydrogen as well as enhanced operator appeal and excellent out of positional capability.
1% nickel deposit. Used in applications where low temperature notch toughness is required. Can be used on weathering types of steel where color match is not required.
All position flux-cored welding electrode for welding the 0.50% Molybdenum steel and other low alloy steels.
Designed as a low Manganese (Mn) replacement for E81T1-K2M products. Meets all requirements of E81T1-K2M classification except for the minimum Mn requirement. This product offers reductions of Mn in the weld fume of 60-80% over a standard E81T1-K2M with low diffusible hydrogen as well as enhanced operator appeal and excellent out of positional capability.
AWS A5.29: E91T1-K2C H8, E91T1-K2M H8 is Flux Cored Welding Wire.All position wire formulated to allow for excellent mechanical toughness properties at lower temperatures in the as welded conditions
Designed for use in the off shore market due to its excellent impact resistance at low temperatures.
AWS A5.20: E70T-4 is Flux Cored Welding Wire.Self-shielding tubular wire designed for high deposition rates. Used for mild steel applications.
All position flux-cored wire used in applications where low temperature notch toughness is required. Can be used on weathering steels when color match is not required.
AWS A5.20: E70T-7 Straight polarity self-shielded tubular wire. Low spatter and easy slag removal for carbon steels.
Excellent for high tensile strength and low temperature impact properties that are needed. The basic slag formulation also ensure that the weld deposit will be low in diffusible hydrogen. Provides great fracture toughness, increased toughness at low temperature and increased resistance to cracking.
All position wire formulated to allow for excellent mechanical toughness properties at lower temperatures in the as welded conditions.
All position gas shielding flux-cored wire designed for welding of offshore jack up rigs and high strength steels such as A514, A710, EQ56, and similar HSLA and Q&T steels
AWS A5.20: E71T-14 is Flux Cored Welding Wire.Higher deoxidizing elements make this an excellent choice for welds on coated materials. It's soft arc makes this a good choice for thin gauge steels.
For applications that require a self shielded high deposition wire with low temperature impact toughness. Designed for use outside.
This wire is used for almost any general purpose welding application and in any position. Works well on coated steels.
For those applications requiring all position capability with low temperature impacts. Designed for use outside.
Designed for use on Grade X70 pipe and below for Onshore Transmission pipelines. Good for variety of structural steel and general fabrication applications. Designed for applications requiring high impact toughness at low temperatures.
AWS A5.29: E71T8-K6J H8 Flux Cored Welding Wire.Designed for use on offshore drilling rigs as well as structural steel and general fabrication applications. Designed for applications requiring high impact toughness at low temperatures.
Designed for use on Grade X65 pipe and below for Onshore Transmission pipelines. Good for variety of structural steel and general fabrication applications. Designed for applications requiring high impact toughness at low temperatures.
AWS A5.29: E81T8-Ni2J H8 Flux Cored Welding Wire.Designed for use on Grade X80 pipe for Onshore Transmission pipelines, as well as structural steel and general fabrication applications. Excellent for applications requiring high impact toughness at low temperatures.
AWS A5. 29: E91T1-K2 MJ H4 Flux Cored Welding Wire.An all-position gas-shielded flux-cored wire that provides excellent mechanical properties. This product maintains acceptable toughness at very low-temperatures, making it desirable for use in the critical applications of the offshore and shipbuilding industries
Metal cored wire for carbon steel application. Excellent impact toughness properties down to -40F.Seamless Wire
AWS A5. 20: E71T-1MJ H4 Flux Cored Welding Wire is a rutile flux cored wire for carbon steel applications. Fast freezing slag for higher deposition rates in all position.
A 120,000 psi tensile, high performance metal cored wire for use with high strength, low alloy steels such as ASTM 514, HY-100 and T1 steels. Diffusible hydrogen levels will be less than 4ml/100g of deposited weld metal giving it more resistance to cracking.Seamless Wire
AWS A5.29: E81T1-Ni1C H4, E81T1-Ni1MJ H4 Seamless Wire Flux Cored Welding Wire.All position flux-cored wire used with mixed gas or 100% CO2 shielding gas in applications where low temperature notch toughness or long stress-relief cycle times are required. 
designed for welding low alloy steels with around a 1% Ni deposit and applications where low temperature toughness is required. Can also be used in some weathering steel applications where color match is not critical.
This wire has a basic slag system and is designed excellent impact properties at low temperatures. Weld metal hydrogens are very low making this wire more crack resistant
FabCOR Element 70C is a mild-steel metal-cored wire designed for the heavy equipment, shipbiulding, railcar and general fabrication industries that along with all the benefits of metal-cored wire also extremely low manganese emissions.
AWS A5. 18: E70C-3C Flux Cored Welding Wire.Metal-cored gas-shielded wire combining the high deposition rates of a flux-cored wire with the high efficiencies of a solid wire. Will improve productivity through increased deposition rates and higher travel speeds. Slag free welds and low Hydrogen weld deposit.
Higher deoxidization elements allow this metal cored wire to have more tolerance for mill scale welding applications
AWS A5.18: E70C-6M H4 Flux Cored Welding Wire.Edge is a metal-cored wire with fewer silicon islands than other metal-cored wires. On clean material, weld bead toe lines are almost completely free of silicon deposits.
AWS A5.18: E70C-GS Flux Cored Welding Wire.Extremely high deposition metal-cored wire designed primarily for Automotive and galvanized applications.
AWS A5.28: E80C-Ni1 H4 Flux Cored Welding Wire.Developed for the welding of nickel-molybdenum steels such as 1/2 Ni/1/4 Mo, 1 Ni/1/4 Mo, and 1 1/2 Ni/1/4 Mo. Can also be used for weathering steel applications where color match is not critical.
Search Products

AWS A5.28: E90C-D2 Flux Cored Welding Wire.Developed for high strength, low alloy steels found in heavy equipment or structural parts.
AWS A5.28: E90C-K3 H4 Flux Cored Welding Wire.Used in the welding of higher strength steels.
AWS A5.28: E100C-K3 Flux Cored Welding Wire.Produces weld metal with a minimum of 100 ksi tensile strength. It has excellent low temperature toughness to -60F.
AWS A5.28: E110C-K4 H4 Flux Cored Welding Wire.A 110,000 psi tensile, high performance metal cored wire for use with high strength, low alloy steels such as ASTM 514, HY-100 and T1 steels. Formulated to have low smoke and fume levels while maintaining excellent chemical and mechanical properties.
AWS A5.28: E80C-Ni2 H4 Flux Cored Welding Wire.For those applications requiring high Charpy impact values at sub-zero temperatures.
AWS A5.28: E90C-D2 H4 Flux Cored Welding Wire.Low alloy metal cored wire designed for welding mild and high strength low alloy steels. Produces .5% Mo weld deposit.
AWS: E70C-6M-H4, E70T15-M21A4-CS1-H4 Metal-Cored Gas-Shielded (GMAW-C), Tianjin, China.It is a mild steel metal-cored wire designed with minimal silicon islands for an exceptionally clean weld surface and minimal post weld clean up.
It is a low alloy metal-cored wire designed with minimal silicon islands for an exceptionally clean weld surface and minimal post weld clean up.
It is a low alloy metal-cored wire designed for high strength welding where tensile requirements of 620 MPa (90ksi) are required.
is a low alloy metal cored wire capable of producing welds with tensile strengths of 760 MPa (110 ksi).
it is a low alloy metal cored wire with low spatter and excellent arc stability.
High deposition metal core wire used in conjunction with  HDT high deposition waveform process solution
Designed to enhance productivity and quality of single pass lap and fillet welds on galvanized and other zinc coated steels (galvannealed).


A mild steel, metal-cored wire that assists efforts to reduce exposure to Manganese.


A mild steel, metal-cored wire designed for superior arc performance in fast-follow, high travel speed applications requiring minimal amounts of spatter.


A mild steel, metal-cored wire designed for superior arc performance in high deposition, high travel speed applications requiring minimal amounts of spatter.


Designed for high deposition, out-of-position welding for structural fabrication in seismic zones. Recommended for single or multiple pass welding of 4.8 mm (3/16 in) and heavier carbon steel.


Designed for high deposition, out-of-position welding for structural fabrication in seismic zones. Recommended for single or multiple pass welding of 4.8 mm (3/16 in) and heavier carbon steel.


The choice for novice or experienced welders looking for an easy to operate self-shielded, flux-cored wire. The excellent arc control and accommodating weld puddle enable operators to make high quality weld deposits regardless of skill level.For training or novice welders while also meeting the mechanical property requirements listed in AWS D1.8.


A versatile wire suitable for all-position welding of light gauge or thin plate. Recommended for maximum plate thicknesses in the range of 7.9 mm (5/16 in) to 12.7 mm (1/2 in).


 It is recommended for single or multiple pass welding on up to 19 mm (3/4 in.) thicknesses.


AWS: BS EN ISO 17633-B Flux Cored Arc Welding Wire , Tianjin, China. Suited to the most demanding vertical and overhead welding applications, including fixed pipework for ASME


AWS: E2209T1-1/4 Flux Cored Arc Welding Wire , Tianjin, China. Designed for Duplex Stainless Pipe, Plate, Fittings and Forgings


AWS: E2594T1-4 Flux Cored Arc Welding Wire , Tianjin, China. Use on 25% Cr super duplex stainless


AWS: E308HT0-1/4 Flux Cored Arc Welding Wire , Tianjin, China. Designed for strength and resistance to corrosion


AWS: E308LT1-1/4 J Flux Cored Arc Welding Wire , Tianjin, China.Controlled Low Ferrite (Range 3-5)
AWS: E316LT1-1/4 Flux Cored Arc Welding Wire , Tianjin, China.Controlled Low Ferrite (Range 3-5)
AWS: E317LT1-1/4 Flux Cored Arc Welding Wire , Tianjin, China.Improved resistance to pitting in high chloride environments
AWS: E347T0-1/4 Flux Cored Arc Welding Wire , Tianjin, China.Used to weld titanium and niobium stabilized 18/8 stainless steel types 321 and 347
AWS: E2594T1-4 Flux Cored Arc Welding Wire , Tianjin, China.Superior resistance to stress corrosion cracking (SCC) and pitting corrosion
AWS: E308LT0-1, E308LT0-4 Flux Cored Arc Welding Wire , Tianjin, China.Smooth arc action with minimal spatter reduces post-weld cleaning
AWS: E308LT1-1, E308LT1-4 Flux Cored Arc Welding Wire , Tianjin, China.Smooth arc action with minimal spatter reduces post-weld cleaning
AWS: E309LT0-1, E309LT0-4 Flux Cored Arc Welding Wire , Tianjin, China.Smooth arc action with minimal spatter reduces post-weld cleaning
AWS: E309LT1-1, E309LT1-4 Flux Cored Arc Welding Wire , Tianjin, China.Smooth arc action with minimal spatter reduces post-weld cleaning
AWS: E316LT0-1, E316LT0-4 Flux Cored Arc Welding Wire , Tianjin, China.Smooth arc action with minimal spatter reduces post-weld cleaning
AWS: E308T1-1/-4, E308LT1-1/-4 Flux Cored Arc Welding Wire , Tianjin, China.has all position welding capability; designed for welding 304L and other common 18/8 stainless steels.
AWS: E71T-9C-H8, E71T1-C1A2-CS1-H8 Flux Cored Arc Welding Wire , Tianjin, China is a mild steel, gas-shielded flux-cored wire designed for the shipbuilding industry to provide high deposition rates and flat bead appearance.
AWS: E81T8-G, E81T8-A5-K8-H8 Flux-cored self-shielded (FCAW-S) Wire, Tianjin, China. Self-shielded electrode designed for welding in structural applications.
Designed to handle poor fit-up on heavy wall tubes and gaps up to 9.5 mm (3/8 in) with 6.4 mm (1/4 in) offset. Recommended for all position welding on unlimited plate thicknesses.
 Designed to produce a nickel bearing weld deposit with impact properties capable of exceeding 27 J (20 ft·lbf) at -29°C (-20°F). It handles poor fit-up in the vertical up position and welds gaps up to 9.5 mm (3/8 in).
A mild steel self-shielded flux-cored wire designed to provide low temperature impact toughness in a variety of offshore applications.Designed to provide optimal weldability in narrow TKY joints and poor fit up condition.
Designed for in-position, high deposition welding on carbon steel. Recommended in single or multiple pass, automatic and semiautomatic welding.


Designed for high deposition rates and fast travel speeds. Recommended for fillet, lap and butt welds on 3.2 mm (1/8 in) and thicker steel, including some low alloy steels in applications without impact strength requirements.
Designed to provide a nominal 1.5% nickel weld deposit with high deposition rates and fast travel. Recommended for flat and horizontal positions in single and multiple pass welding.
Designed for very high deposition rates and increased resistance to hydrogen cracking and porosity on steel containing sulfur or contaminates. Recommended for single or multiple pass welding on carbon steel and some low alloy steels in applications without impact strength requirements.
Designed for high speed single pass welding applications. Recommended for flat and horizontal positions with maximum steel thickness up to 4.8 mm (3/16 in).
Designed for high deposition rates at high speeds. Recommended for single pass welding on material thicknesses of 2.8 mm (0.110 in) or greater.
Has the portability of stick electrode and the productivity of wire. It is recommended for hot, fill and cap pass welding of up to X70 grade pipe.
Has the portability of stick electrode and the productivity of wire. It is capable of producing impact values of 27 J (20 ft·lbf) @ -29°C (-20°F). Recommended for hot, fill and cap pass welding of up to X80 grade pipe.
Has been micro-alloyed to be capable of exceeding impact values of 68 J (50 ft·lbf) @ -29°C (-20°F). It is recommended for hot, fill and cap pass welding of up to X80 grade pipe.
Designed to create high strength weld deposits with yield strength test results exceeding minimum AWS requirements. Recommended for API Pipe Grade X80.
Designed for vertical down, hot, fill and cap passes on standard cross-country pipelines and arctic grade pipe. Recommended for API Pipe Grades X42 up to undermatching X70.
Designed for high speed welding of specialty coated steels. Recommended for single pass welding on material thicknesses from 0.8 to 4.8 mm (0.030 to 3/16 in).
Designed specifically for use with high Argon mixed gas. Shipbuilders and structural fabricators like it because it runs well – it's our best running E71T-1 for high Argon gas blends,
AWS: E71T-1M-JH4, E71T-1C-H4, E71T1-M21A2-CS1-H4, E71T1-C1A0-CS1-H4has a copper coating that offers superior feedability and extended contact tip life.


 a mild steel, gas-shielded flux-cored wire designed to protect the flux core from environmental exposure helping to maintain low diffusible hydrogen and extend shelf life.


A mild steel, gas-shielded flux-cored wire designed to provide the high deposition rates and low temperature impact toughness required in many heavy fabrication applications.


Our best running E71T-12 product because of its superior arc characteristics and high impacts in a variety of applications, including offshore, tank and pressure vessel fabrication.


AWS: E81T1-Ni1M-JH4, E81T1-M21A6-Ni1-H4 Innovative design capable of superior toughness at-60°F


AWS: E81T1-Ni1C-JH4, E81T1-C1A6-Ni1-H4 Innovative design capable of superior toughness at-60°F


AWS: E81T1-K2M-JH4, E81T1-M21A6-K2-H4 Innovative design capable of superior toughness at-60°F
AWS: E81T1-K2C-JH4, E81T1-C1A6-K2-H4 Innovative design capable of superior toughness at-60°F
AWS: E91T1-K2M-JH4, E91T1-M21A6-K2-H4 Innovative design capable of superior toughness at-60°F
AWS: E91T1-K2C-JH4, E91T1-C1A6-K2-H4 Innovative design capable of superior toughness at-60°F
AWS: E101T1-K3M-JH4, E101T1-M21A6-K3-H4 Innovative design capable of superior toughness at-60°F
AWS: E111T1-K3M-JH4, E111T1-M21A6-K3-H4 Innovative design capable of superior toughness at-60°F


AWS: E121T1-GM-H4, E121T1-M21A6-K3-H4 Innovative design capable of superior toughness at-60°F


has excellent slag detachability, even in deep or narrow grooves.High dHigh deposition in the flat and horizontal positions.


Capable of producing low diffusible hydrogen levels and high deposition rates. It is recommended for both single or multiple pass welding in either semi-automatic or automatic applications.


AWS: E80T1-Ni1C-JH8, E80T1-C1A4-Ni1-H8 Flux-cored (FCAW-G) Wire has excellent operator appeal and slag detachability.Excellent operator appeal and slag detachability.
AWS: E80T1-Ni1M-JH8, E80T1-M21A4-Ni1-H8 Flux-cored (FCAW-G) Wire has high deposition in the flat and horizontal positions.High deposition in the flat and horizontal positions.
AWS: E80T1-Ni1C-JH8, E80T1-C1A4-Ni1-H8 Flux-cored (FCAW-G) Wire has excellent operator appeal and slag detachability.Excellent operator appeal and slag detachability.
AWS: E71T-1M-H8, E71T1-M21A0-CS1-H8 Flux-cored (FCAW-G) Wire is the lowest Manganese Generation Rate (MnGR) of any similarly classified electrode.
AWS: E71T-1C-H8, E71T1-C1A0-CS1-H8 Flux-cored (FCAW-G) Wire is designed for welding with 100% COsub2/sub shielding gas.
AWS: E81T1-Ni1M-JH4, E81T1-M21A4-Ni1-H4 Flux-cored (FCAW-G) Wire is designed for high strength, low-alloy applications using 75% Argon/25% CO2.
AWS: E81T1-Ni1C-JH4, E81T1-C1A4-Ni1-H4 Flux-cored (FCAW-G) Wire is designed for high strength, low-alloy applications using 100% CO2 shielding gas.
AWS: E81T1-K2C-JH4, E81T1-C1A5-K2-H4 Flux-cored (FCAW-G) Wire is capable of producing weld deposits with impact toughness exceeding 111 - 141 J (82 - 104 ft·lbf) at -40°C (-40°F).
AWS: E81T1-Ni2M-JH4, E81T1-M21A6-Ni2-H4 Flux-cored (FCAW-G) Wire exhibits superior crack resistance due to low diffusible hydrogen levels (4 mL/100 grams of weld deposit max).
AWS: E81T1-Ni2C-JH4, E81T1-C1A6-Ni2-H4 Flux-cored (FCAW-G) Wire is a 100% CO2 welding wire that exhibits robust low temperature impact properties.
AWS: E81T1-GM, E81T1-M21A4-K11 Flux-cored (FCAW-G) Wire is designed for hot, fill and cap pass welding on up to X70 grade pipe.
AWS: E101T1-GM, E101T1-M21A4-K11 Flux-cored (FCAW-G) Wire is designed for hot, fill and cap pass welding on up to X80 grade pipe.
AWS: E71T-12C-JH8, E71T1-C1A5-CS2-H8 Flux-cored (FCAW-G) Wire has premium arc performance and fast freezing slag.
AWS: E71T-12M-JH8, E71T1-M21A5-CS2-H8 Flux-cored (FCAW-G) Wire is capable of meeting 20 ft-lbs at -50°F in both the as-welded condition and stress relieved conditions.
AWS: E81T1-B2C/M-H4 Flux-cored (FCAW-G) Wire is designed for strength and resistance to corrosion.
AWS: E71T-9C-H8, E71T-9M-H8, E71T1-C1A2-CS1-H8, E71T1-M21A2-CS1-H8 Flux-cored (FCAW-G) Wire has a smooth arc transfer, low spatter and good bead appearance.
AWS: E91T1-B3C/M-H4 Flux-cored (FCAW-G) Wire is made using a high purity steel sheath with high deposition rates. Used for welding 2 1/4% Cr / 1% Mo low alloy steels.
AWS: E91T1-GM Flux-cored (FCAW-G) Wire .All position gas shielded 1% Ni and 0.4%Mo alloyed flux cored wire for offshore, pipeline and similar applications
AWS: E71T-9C-J, E71T-9M-J, E71T1-C1A4-CS1-H16, E71T1-M21A4-CS1-H16 Flux-cored (FCAW-G) Wire is an overall performer - from excellent feedability to good arc performance.