AWS ER70S-6 CO2 Gas shielded welding wire is a kind of welding wire, also called Mag/Mig welding wire is a kind of welding wire, also called Mag/Mig welding wire, Gas Metal Arc Welding, (GMAW) which is matched with CO2 gas or Arc gas in welding. It has strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
It is used to welding carbon steels and 500Mpa high strength steels, used in car, building, ships and bridge. Can also be used for speed welding of sheet and pipes.
Our advantages is stable arc, little spatter, less smoke; higher deposition efficiency; excellent welding performance; easy restrike.
CO2 Gas shielded welding wire
Standard: AWS A5.18 ER70S-6, GB ER50-6, DIN SG2, BS A18, JIS YGM12
Sizes: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packaging Details: OEM acceptable
Black and white plastic spools D100, D200, D270, D300
D100, 1KG/spool, 1000spools/pallet
D200, 5KG/spool, 200spools/pallet
D270, 15KG/spool, 72spools/pallet
D300, 15KG/spool, 72spools/pallet
Metal spools K300
K300, 15KG/spool, 72spools/pallet
Drum packing, 250KG/drum
Payment terms: 100% LC at sight or 30% TT in advance balance against copy of BL.
Trade terms: FOB, CFR, CIF, Loading Port: xingang, tianjin, China
Delivery Detail: Within 15 days after confirmation
Key words: MIG welding wire, MAG welding wire, CO2 Gas shielded welding wire, Gas Metal Arc Welding ,GMAW, Gas Tungsten Arc Welding ,GTAW,AWS ER70S-6, GB ER50-6, G3Si1, SG2, ER70S-6, DIN SG2, BS A18, JIS YGM12, welding wire



AWS A5.18 ER70S-6
Welding Wire AWS A5.18 ER70S-6
MIG welding wire AWS A5.18 ER70S-6,is a kind of carbon steel shielded welding wire. The melting speed of welding wire is fast when welding. It has stable arc, low spatters and beautiful appearance. Good corrosion-resistant on surface of base material. Decrease the probability of blowhole formation. All position welding has good performance CO2 or Ar+CO2 can be used as shielded gas.
Welding Wire AWS A5.18 ER70S-6
Application
AWS A5.18 ER70S-6 
1. Used for welding all kinds of 500MPa structural steel parts.
2. Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition (%)
Reference Current (DC+)
Welding Positions:
Notes:
1.The welding electrodes should be preheated 2 hour at 300~350℃ before welding.
2.The impurities such as rust, oil stains and moisture must be cleared off of the work piece.
Mechanical Properties of Deposited Metal (Ar+20%CO2 Gas shielded)

Chemical Composition

C

Mn

Si

S

P

Ni

Cr

Mo

V

Cu

Guarantee Value

0.06~0.15

1.40~1.85

0.80~1.15

≦0.025

≦0.025

≦0.15

≦0.15

≦0.15

≦0.03

≦0.50

General Result

0.077

1.45

0.87

0.013

0.012

0.017

0.031

0.002

0.004

0.125

Test Item

Rm(N/mm2)

Rel/Rp0.2(N/mm2)

A (%)

KV2(J)-40℃

Guarantee Value

≧500

≧420

≧22

≧47

General Result

555

450

29

77、95、83

Size(MM)

CURRENT range (AMPS)

GAS flow rate(L/Min)

Φ0.8

50~100

15

Φ1.0

50~220

15~20

Φ1.2

80~350

15~25

Φ1.6

170~550

20~25