EN 760: SA FB 2 DC gives excellent slag removal without slag residuals – in the 1st layer on preheated substrates as well as in subsequent layers or when joint cladding. Smooth weld bead finish and notch–free transitions are further features when appropriate process parameters are applied.
High basic, agglomerated and neutral flux (without alloy–compensation) designed for overlay welding and joint cladding together with stainless strip electrodes of the Cr–, CrNi(Mo)–steel types.
A semi-basic flux suitable for high speed welding with single and multi-wire (up to 5 wires) submerged-arc processes. EN 760: SA AB 1 66 AC H5 is designed for pipe-welding and vessels of small diameter (>300 mm) and is especially recommended for spiral pipe fabrication employing the two-run technique. Weld bead performance and slag release are excellent providing flat welds with low reinforcement and flat weld interfaces free from undercut.
EN 760: SA CS 3 NiMo DC gives excellent slag removal without slag residuals, in the 1st layer on preheated substrates as well as in subsequent layers. The flux has low hydrogen potential, which makes it most suitable for overlay welding of heat resistant steels such as A387–types.
Agglomerated, semi-basic, Calcium-Silicate flux with Manganese support for SA-overlay welding and shape-forming using single or multiwire (TWIN-ARC) processes. EN 760: SA CS 1 75 AC is particularly designed for the repair of worn pistons for large ship diesel engines.
EN 760: SA FB 1 55 AC is a fluoride-basic flux with high basicity and low impurity levels such as P and S. As a result of low oxygen levels in the weld deposits uniform mechanical properties with high toughness values at low temperature are achieved.
A semi-basic flux for joint welding of high quality steel pipes for pipeline transportation systems in the oil and gas industries. Especially recommended for multi-wire (3 up to 5 wires) submerged arc processes in the two-run technique.
A semi-basic flux suitable for high speed welding with single and multi-wire submerged-arc processes.
EN 760: SA AB 1 67 AC H5 is designed for spiral pipe fabrication employing the two-run technique. Weld bead performance
EN 760: SA AB 1 67 AC H5 is an agglomerated aluminate-basic flux with high current-carrying capacity, specially designed for the welding of windmill towers using tandem – arc.
Versatile flux for joint welding and surfacing with wire or strip electrodes. EN 760: SA AB 1 76 AC H5 is suitable for high speed welding of butt and fillet welds with single and multi wire processes.